90 ℃ Environmental Friendly Product PVC Plastic Compound Granuel Sheath Material T-PV006

90 ℃ Green Environmental  Plastic Compound Base on PVC resin, this product is PVC sheath material made by mixing, plasticizing, and granulating with plasticizers, stabilizers, and other additives.

Categories ,
Inquiry
Plastic Compound Application
Power & Cable Sheath/Jacket   （wire core working temperature 90 ℃)

Appearance
90 ℃ PVC flame retardant sheath material should be made into uniformly sized particles with a particle size of 4 mm × 4 mm × 3 mm, or ф 4× (2-4) mm. Good plasticization, uniform color, and no obvious impurities.
Color
The color is determined through negotiation between the supply and demand parties.

Technical Analysis
Physical Property
Form -1

Technology Parameter

No. Inspection items Standard request Test method Typical value
一 Technical Index
1 Density                                       g/ cm3 / GB  1033 1.45
2 Tensile strength                        MPa ≥16 GB  1040 18
3 Elongation at Break                       % ≥180 GB  1040 250
4 Hot deformation rate   （90℃ ×4 h）% ≤40 GB8815 20
5 Brittle temperature

Test temperature-25℃

 Failed No.≤15/30 GB5470 Pass
6 200 ℃ static thermal stability       min ≥80 GB8815 88
7 Volume Resistivity at 20℃      Ω .m ≥1× 109 GB/T  1410 5×109
8 Dielectric Strength                       MV/m ≥18 GB/T1408. 1 20
Thermal aging property 100±2℃ , 240h
Tensile strength                        MPa ≥16 Pass
 9 Max Variation on Tensile Strength % ±20 GB1040 Pass
Elongation at break                       % ≥180
Max Variation on Elongation at break  % ±20
 10     Thermal   aging
quality loss		 ℃ 100±2 GB/T2951
h 240
Quality loss
g/m2		 ≤15 12
  二     Quality of Appearance
     1 Appearance Extruded lines
are smooth		 Eye survey
     2 Color Consistent color tone Eye survey
Standard deviation ≤1.5 Colorimeter
*Note：

1   The extruded lines are smooth, and no more than 3 floating points with a diameter ≥1. 0mm are allowed
within 1 meter.No particles ≥ 3. 0mm are allowed.
2  All products shall undergo initial inspection upon startup, including appearance, color, density, etc.
3  If the first sample test fails, a retest is required, and the result of the second test is the judgment
standard.

Plastic Compound Processing

Processing
Using a general extruder for processing, L/D≥20
Adjust appropriately according to the equipment and extrusion status.

The following temperature profile of extruder is recommended:
 Zone Zone 1 Zone 2 Zone 3 Zone 4 Zone 5 Head     Die
    Temperature
℃		 140 145 155 165 170 175 175
Storage and transport
Plastic Compound T-PV002 should be packaged in moisture-proof packaging. With polyethylene film bags for the inner bag and kraft paper composite bags for the outer bag, with a net weight of (25.0 ± 0.2) kg per bag. Other packaging methods agreed upon by both the seller and the purchaser are allowed.
During the transportation of the product, it should not be damaged by abnormal conditions. Such as sun, rain, and immersion in water. It should be kept clean, dry, not contaminated, and the packaging should be kept intact.
The product should be stored in a clean, cool, dry, and ventilated warehouse. And the storage period should not exceed six months from the date of production.